| 摘要 |
PCT No. PCT/SE91/00686 Sec. 371 Date Apr. 15, 1993 Sec. 102(e) Date Apr. 15, 1993 PCT Filed Oct. 11, 1991 PCT Pub. No. WO92/06810 PCT Pub. Date Apr. 30, 1992.During production of ductile cast iron, controlling and correcting the composition of the cast iron melt, including extracting a sample from the melt, the mother melt, and adding an amount of an oxide, a sulphite or an oxy-sulphide with the ability to oxidize an amount of the modifying agent present in the sample and corresponding to the fading rate expected to occur during the casting process as a whole. The sample is permitted to solidify in a sample vessel equipped with two thermocouples, one in the center of the sample vessel and the other in the vicinity of the sample vessel wall. The temperature and time are recorded during the process of solidification in a manner known per se and nodularity is calculated. If the amount of modifying agent is too low to secure a fully nodular graphite throughout the whole casting period, an appropriate amount of modifying agent is added. |