| 摘要 |
A method of producing clad steel plate comprises the steps of preparing an assembly slab by superposing a stainless-steel or nickel alloy cladding material onto base metal consisting, by weight, of 0.020 to 0.06% carbon, 0.05% or less silicon, 1.0 to 1.8% manganese, 0.03% or less phosphorus, 0.005% or less sulfur, 0.08 to 0.15% niobium, 0.005 to 0.03% titanium, 0.05% or less aluminum, 0.002 to 0.006% nitrogen, and one or two elements selected from among a group consisting of 0.05 to 1.0% nickel, 0.05 to 1.0% copper, 0.05 to 0.5% chromium, 0.05 to 0.3% molybdenum and 0.001 to 0.005% calcium, with the balance being iron and unavoidable impurities, and welding its periphery; heating the slab to 1100 to 1250 DEG C; rolling the slab at a reduction ratio of 5 or more and a rolling finish temperature of 900 to 1050 DEG C; air cooling for 60 to 200 seconds; cooling the slab from a temperature of at least 750 DEG C to 550 DEG C or below at a cooling rate of 5 to 40 DEG C/sec, and following this by air cooling. |