| 摘要 |
A heat insulating material and a structure made therefrom, wherein the insulating material is adapted for use in the wet process in addition to the dry process in the form of a molded plate, has a heat insulation performance similar to that of an organic heat insulating material and a flame retardation performance equal to that of a conventional inorganic heat insulating material, and further has a higher strength than that of conventional materials. A heat insulating material of the invention comprises a mixture of 100 parts by weight of cement with 3 to 50 parts by weight in terms of solid content of a synthetic resin emulsion, 1 to 20 parts by weight of organic microballoon, 0.3 to 5 parts by weight of carbon fiber and 10 to 200 parts by weight of inorganic microballoon. Another heat insulating material of the invention comprises a mixture of 100 parts by weight of cement with 3 to 50 parts by weight in terms of solid content of a synthetic resin emulsion, 1 to 20 parts by weight of organic microballoon and 0.3 to 5 parts by weight of carbon fiber. |