METHOD OF METALLIZING OXIDE CERAMIC WITH EXCELLENT HERMETIC SEALING AND BRAZING PROPERTIES |
摘要 |
<p>A method of metallizing an oxide ceramic with excellent hermetic sealing and brazing properties, comprising the steps of applying to a sintered oxide ceramic a first paste prepared by mixing with an organic vehicle a powder mixture composed of 70 to 95 wt% of a wolfram powder having an average particle diameter of 10 mu m or less and 30 to 5 wt% of a glass powder having an average particle diameter of 10 mu m or less and a melting point of from 1100 to 1300 DEG C; drying the first paste-applied ceramic to form a primary coating on the ceramic; applying to the primary coating a second paste prepared by mixing with an organic vehicle one or more powders selected from the group consisting of nickel, nickel oxide, and nickel salt powders; drying the second paste-applied ceramic to form a final coating on the primary coating; and firing the ceramic having the primary and the final coatings thereon at a temperature of from 1200 to 1400 DEG C in an atmosphere having a H2/H2O ratio higher than 1 and lower than 100000 in terms of partial pressure ratio.</p> |
申请公布号 |
EP0384950(A3) |
申请公布日期 |
1991.07.03 |
申请号 |
EP19890112958 |
申请日期 |
1989.07.14 |
申请人 |
NIPPON STEEL CORPORATION |
发明人 |
TANIGUCHI, HIROKAZU C/O NIPPON STEEL CORPORATION;KONYA, SHOGO C/O NIPPON STEEL CORPORATION;OKAMOTO, AKIRA C/O NIPPON STEEL CORPORATION |
分类号 |
C04B41/52;C04B41/89;H05K1/09;H05K3/10;H05K3/24;(IPC1-7):C04B41/52;C04B41/51;C04B41/45 |
主分类号 |
C04B41/52 |
代理机构 |
|
代理人 |
|
主权项 |
|
地址 |
|