摘要 |
A thermoformable polyaryletherketone sheet of a thickness of about 625-5000 micrometers, having repeating units derived from diphenyl ether and terephthalyl and isophthalyl groups, especially a polyetherketoneketone in which the terephthalyl to isophthalyl isomer ratio is about 70:30 to 0:100, especially 60:40 to 50:50, which thermoformable sheet has a crystallinity of 5% of less, can be fabricated into three-dimensional articles such as, e.g., panels and ducts for aircraft interiors having good formability and mold replication. |