| 摘要 |
The invention relates to a process for obtaining an Al alloy of the 7000 series (Al-Zn-Cu-Mg) of high mechanical strength and good ductility by spray deposition; the process is aimed at obtaining Al alloys having a breaking load of >/= 800 MPa and an elongation greater than or equal to 5%, or obtaining these same alloys reinforced with ceramic particles. …<??>The invention accordingly consists in:… 1. forming, by spray deposition, a massive alloy of the following composition by weight: Zn from 8.5 to 15%; Mg from 2.0 to 4.0%; Cu from 0.5 to 2.0%; at least one of the following 3 elements: Zr from 0.05 to 0.8%; Mn from 0.05 to 1.0%; Cr from 0.05 to 0.8%, with Zr + Mn + Cr </= 1.4%; Fe up to 0.5%; Si up to 0.5%; other elements </= 0.05% each, </= 0.15% in total; remainder Al.… 2. hot transforming of the body thus obtained at between 300 and 450 DEG C and optionally in the cold and… 3. treating the product thus obtained by dissolution, quenching and annealing. |