摘要 |
<p>In the prepn. of the first layer of organic optics, under pressure and inert atmos., from (meth) acrylic monomers, a mixt. comprising at least a prepolymer of these monomers, having a conversion degree of at least 30%, a polymsn. initiator and a chain transfer agent, is placed in a reactor and polymerised under inert atoms. and pressure of at least 5 bars, pref. at least 15 bars. Also claimed are preocesses (see below) for depositing a new layer on the above layer. The mixt. to be polymerised is pref. kept under inert atomos. pressure of at least 15 bars while simultaneously:- keeping the temp. at 30-100 deg.C until conversion rate reaches 95-+/-2%, raising the temp. to 120-160deg.C until conversion rate reaches 97-99% and continuing to raise the temp. to 160-180deg.C for at least 2 hrs. and cooling to form a solid organic optics.</p> |