This invention is directed to the production of nitride-based ceramic bodies selected from the group of AlN and Si3N4 which can be sintered to near theoretical densities at temperatures at least 200 DEG C lower than those required for the pure materials. Such bodies are densified through the addition of a metal fluoride selected from the group of aluminum, barium, calcium, strontium, yttrium, the lanthanide rare earth metals, and mixtures thereof. Up to 80% by weight of said metal fluoride may be included but, generally, such additions will be held between 5-30% by weight. AlN bodies exhibiting very high thermal conductivity can be prepared by sintering with a metal fluoride selected from the group of barium, calcium, strontium, yttrium, the lanthanide rare earth metals, and mixtures thereof. |