Polyacrylonitrile articles, such as filaments, tapes and films, having high tensile strength and modulus, and prepared by adding to a solution of polyacrilonitrile with a molecular weight above 3x105, preferably above 5x105, a minor amount of a bivalent metal compound, converting the solution into a solvent containing article, cooling this article to form a gel article, removing from this gel the solvent and metal compound, and stretching the resulting article at increased temperature. With this process filaments with a tensile strength above 1.2 GPa and a modulus above 16 GPa can be obtained. |