Superelastic dental Au-Cu-Zn alloys characterizing that it is in a range defined by point A (63 wt % Au, 11 wt % Cu, 26 wt % Zn), Point B (55 wt % Au, 17 wt % Cu, 28 wt % Zn), Point C (55 wt % Au, 18 wt % Cu, 27 wt % Zn), Point D (63 wt % Au, 14 Wt % Cu, 23 wt % Zn), Point E (65 wt % Au, 12 wt % Cu, 23 wt % Zn) and Point F (65 wt % Au, 11 wt % Cu, 24 wt % Zn), in the Au-Cu-Zn ternary diagram of FIG. 1.
|