| 摘要 |
A sintered silicon nitride article exhibiting highly desirable mechanical strength at room temperature and at elevated temperatures as well and a method for the production thereof are disclosed. The sintered ceramic article is obtained by firing a ceramic mixture comprising not more than 10% by weight of the oxide of a rare earth element and not more than 10% by weight of aluminum nitride as additives and the balance of silicon nitride powder obtained by the silicon diimide thermal decomposition method and having an alpha -phase silicon nitride content of not less than 95%, a carbon content of not more than 0.1%, and an oxygen content of not more than 1.5%. |