| 摘要 |
PURPOSE:To obtain the titled composite superior in moldability and capable of being burnt sufficiently in a short time, by specifying a compsn. ratio composed of surface treated sintering material powder and syndiotactic 1.l2 -polybutadien and organic oxide. CONSTITUTION:The composite is composed of sintering material consisting of metal and/or inorganic compound having 0.1-500mu average particle diameter, and >=600 deg.C m.p., syndiotactic 1.2 - polybutadiene having 0.1-30 g/10min melt index and 10-45% crystallinity, and organic peroxide, said sintering material is 50-95 wt.% compsn. ratio to total quantity of this and syndiotactic 1.2 -polybutadiene, organic peroxide is 0.1-10 wt. part compsn. ratio to said total quantity; 100 wt. part, and surface of sintering material is treated with 0.1-10 wt. part of higher fatty acid and/or metal salt to said sintering material; 100 wt. part. |