<p>A high solids content, relatively low viscosity, organic solvent solution of polyester magnet wire enamel is described. The enamel is a tris (hydroxy-ethylisocyanurate) polyester having a ratio of hydroxyl to carboxyl groups of 1.65 to 2.0:1 and a hydroxyl number of 216 to 316. Such enamels are produced with solids contents of about 50 to about 70% by weight and viscosity less 1,500 cps at 200 DEG F. The method of making such enamel by reacting a glycol, tris (hydroxy-ethylisocyanurate), and an aromatic diacid or diester in the presence of a titanate catalyst is also described.</p> |