| 摘要 |
In a process for the production of a grain-oriented silicon steel strip, a slab is heated, hot-rolled, cold-rolled, and subjected to a decarburization annealing and secondary recrystallization annealing steps. Grain coarsening is likely to occur during the high temperature heating and remain in the final product as streaks. The secondary recrystallization is, therefore, incomplete due to the streaks. In the hot rolling, an asymmetric flow, is applied to the steel, so as to eliminate the streaks and, hence, to obtain excellent magnetic properties. |