摘要 |
<p>Nickel-chromium-cobalt base casting alloys having compositions within the range (in percent by weight) Cr 20-23%, Co 17-23%, W 1-2.5%, Mo 0-0.5%, Nb 0.4-1.2%, Ta 0.6-1.4%, Ti 2,95-3.85%, Al 1.6-2.8%, Hf 0.3-1.3%, Zr 0.005-1%, B 0.001-1%, C 0.01-0.25%, balance Ni and impurities, wherein the contents of Nb, Hf, Ti and Al are further specifically correlated, exhibit at high temperatures a combination of good resistance to corrosion and very high creep-rupture lives, particularly when directionally solidified. The alloys are useful as materials for cast blades and vanes for gas turbines for marine and land-based service.</p> |