| 摘要 |
LA PRESENTE INVENTION CONCERNE DES FILS ET FIBRES A BASE DE POLYCHLORURE DE VINYLE ATACTIQUE. ILS POSSEDENT UN TAUX DE RETRAIT RESIDUEL DANS L'EAU BOUILLANTE INFERIEUR A 3, UN MODULE D'ELASTICITE SUPERIEUR OU EGAL A 2KNMM, UN INDICE D'ORIENTATION DES ZONES CRISTALLINES EGAL OU SUPERIEUR A 70, ET UN INDICE D'ORIENTATION DES ZONES MESOMORPHES EGAL OU SUPERIEUR A 8, CELUI DES ZONES AMORPHES EGAL OU SUPERIEUR A 5.ILS SONT OBTENUS PAR FILAGE ET ETIRAGE DE MANIERE CONNUE, PUIS STABILISATION SOUS TENSION A UNE TEMPERATURE COMPRISE ENTRE 105 ET 130C, EN PRESENCE DE VAPEUR SOUS PRESSION PENDANT 1 A 3 SECONDES PUIS RETRACTION EN MILIEU FLUIDE AQUEUX A UNE TEMPERATURE COMPRISE ENTRE 98 ET 130C.DE TELS FILS ET FIBRES SONT AVANTAGEUSEMENT UTILISABLES DANS DE NOMBREUX DOMAINES TEXTILES SEULS OU EN MELANGE AVEC D'AUTRES FIBRES. |