| 摘要 |
<P>EN VUE DE CONFERER AUX TOLES A LA FOIS UNE HAUTE LIMITE D'ELASTICITE ET UNE BONNE APTITUDE A L'EMBOUTISSAGE, ON MET EN OEUVRE UN ACIER TITRANT AU MAXIMUM 0,16 C, 2,0 MN, 0,55 SI ET 0,03 A1 AU MINIMUM AINSI QU'EVENTUELLEMENT JUSQU'A 0,05 NB ET 0,1 V, ON PORTE LA TOLE RAPIDEMENT A UNE TEMPERATURE SUPERIEURE A CELLE DU POINT A3. C. A D. ENTRE 700 ET 900C, DANS UN SYSTEME A REFROIDISSEMENT RAPIDE 6-7 ON MAINTIENT LA TOLE A CETTE TEMPERATURE AUSSI LONGTEMPS QUE POSSIBLE, SANS QU'IL Y AIT GROSSISSEMENT DU GRAIN. ON EFFECTUE ENSUITE UN REFROIDISSEMENT DE 100CSEC JUSQU'A UNE TEMPERATURE INFERIEURE A CELLE DU POINT ARL ET ON LAISSE REFROIDIR LA TOLE A UNE VITESSE DE L'ORDRE DE 1CSEC.</P><P>LE PALIER DU REVENU SE SITUE ENTRE 550 ET 650C, DE PREFERENCE A 600C ET IL EST REALISE EN IMMERGEANT LA TOLE DANS UN MILIEU SOIT LIQUIDE, P. EX. UN BAIN DE SELS OU DE METAL, SOIT GAZEUX.</P>
|