| 摘要 |
A method for producing optical glass, which comprises charging a mixed solution capable of forming a high-silica-content gel by hydrolysis reaction into a vessel, the inner wall face of which is composed of a material unwettable to the mixed solution, such as a fluorocarbon resin or silicone resin, causing gelation of the mixed solution in the vessel, drying the obtained gel, and heating and sintering the obtained dry gel. When electrodes are placed in the mixed solution at the gelation step and an electric voltage is applied, the time required for formation of the gel is shortened. Furthermore, at the gel-drying step, if the amount of materials evaporated from the gel is detected or the weight of the gel is measured, the detected amount of the evaporated materials or the change of the weight of the gel is fed back to a factor regulating the drying speed, such as the drying temperature to control the drying speed to an appropriate level.
|