<P>DANS CE PROCEDE, LA MATIERE EST DE L'ACRYLONITRILE COPOLYMERISE AVEC UNE FAIBLE QUANTITE D'UN MONOMERE ACRYLIQUE TEL QUE L'ACRYLATE DE METHYLE. L'OXYDATION DE LA FIBRE EST EFFECTUEE A UNE TEMPERATURE ELEVEE EN PRESENCE D'UN ACIDE CARBOXYLIQUE, AUTRE QUE L'ACIDE FORMIQUE, OU DE SON ANHYDRIDE IMPREGNE DANS LA FIBRE. ON SUPPOSE QUE L'ACIDE ETOU SON ANHYDRIDE QUI EST FORME A LA TEMPERATURE D'OXYDATION SERVENT DE PLASTIFIANT ET DIMINUENT LA LIMITE ELASTIQUE DE LA FIBRE ET AUGMENTENT SA PLASTICITE, DE SORTE QUE LES FIBRES PEUVENT ETRE ETIREES MEME DE 300, OU DAVANTAGE, EN PRESENCE DE L'ACIDE ETOU DE SON ANHYDRIDE PENDANT L'OXYDATION, AMELIORANT AINSI L'ELASTICITE ET LA RESISTANCE A LA TRACTION.</P><P>UTILISATION DE CE PROCEDE POUR LA FABRICATION DE FIBRES DE CARBONE DE DIAMETRE PLUS PETIT ET AVEC UN MODULE D'ELASTICITE ET UNE RESISTANCE A LA TRACTION, AMELIORES.</P>
|