Process for preparing polyimide solution

摘要

A polyimide solution is prepared by a process wherein a tetracarboxylic acid ingredient containing at least about 80% by mole of 3,3',4,4'-biphenyltetracarboxylic acid or its functional derivative and an aromatic diamine ingredient containing at least about 50% by mole of 4,4'-diaminodiphenyl ether are polymerized at from about 100 DEG to 300 DEG C. in phenol or a halogenated phenolic compound; the amount of the acid and diamine ingredients being approximately equimolar to each other; whereby polymerization of the tetracarboxylic acid ingredient and the aromatic diamine ingredient is effected while being accompanied by imidation. Preferably, the polymerization accompanied by imidation is effected in a manner such that at least a second half of the polymerization is carried out in a closed reaction system. The resulting polyimide solution is suitable for making therefrom shaped articles, such as films, possessing excellent mechanical properties.