ELEKTRONENROEHREN-KATHODE UND IHRE HERSTELLUNG

摘要

An electron tube cathode in such a structure comprising a Ni-W-Zr alloy (W content: 20-28 wt. %) having a grain size of 4-10 mu m as a base metal, a 1,000-2,000 A-thick Pt film provided on the surface of the base metal, and an electron emitting material layer consisting of alkaline earth metal oxide provided on the Pt film has less emission lowering and less peeling of the electron emitting material layer, even if placed in a long time service. The electron tube cathode can be produced according to a method comprising (i) a step of annealing a base metal of Ni-W-Zr alloy (W content: 20-28 wt. %) at 1,000 DEG -1,200 DEG C., (ii) a step of providing a 1,000-2,000 A thick Pt film on the surface of the base metal, and (iii) a step of providing an electron emitting material layer consisting of alkaline earth metal oxide on the Pt film.