| 摘要 |
A method for producing a low carbon deep drawing quality steel or high strength steel in the form of a strip or sheet. At least one of carbide or nitride forming elements is added to the low carbon steel to provide therein 0.015 to 0.10% Sol Al, 0.01 to 0.10% Nb, 0.01 to 0.10% Ti and 0.01 to 0.15% V. The steel is cast or bloomed to form a slab which is held above the Ar3 point for keeping the carbide and nitride forming elements in a dissolved state. Then, without allowing the temperature to fall below the Ar3 point, hot rolling and hot finishing rolling are directly carried out at a temperature above the Ar3 point. Thereafter, if necessary and desirable, the thus-rolled slab or sheet is subjected to cold rolling and annealing. |