<p>A flexible double-layer polypropylene laminate consisting of a bioriented film consisting essentially of isotactic polypropylene with an atactic polypropylene content of less than 6% by weight and an intrinsic viscosity (standard ASTM D 1601) of from 1.5 to 3.0 dl/g, adhesively bonded with a non-oriented film consisting essentially of a mixture of isotactic polypropylene and atactic polypropylene, the latter in an amount of from 15 to 30% by weight of the total weight of the said mixture, the isotactic polypropylene of said mixture having an intrinsic viscosity (standard ASTM D 1601) of from 1.0 to 1.5 dl/g and the atactic polypropylene of said mixture having a density (standard ASTM D 1505) of from 0.855 to 0.865 g/cm3 and a viscosity at 160 DEG C. of from 3,000 to 10,000 cps.</p> |