| 摘要 |
A process for the production of a fine-celled foam from a mixture of a polyolefin, a peroxide capable of peroxidically cross-linking the polyolefin and a principal blowing agent having a decomposition point or decomposition range above about 190 DEG C, wherein a further blowing agent, an auxiliary blowing agent, having a decomposition range of from 130 DEG to about 190 DEG C is added in a quantity of from 0.1 to 1.5 percent by weight, based on said principal blowing agent, to said mixture, the mixture thus obtained is worked up under such conditions that neither cross-linking nor appreciable foaming takes place to a moulding, which is subsequently, cross-linked and foamed by heating to temperatures above 190 DEG C. |