| 摘要 |
PROBLEM TO BE SOLVED: To easily obtain a conductive fluororubber sheet having an excellent beauty and large area by molding specific conductive fluororubber composition by a pressing pressure of specific planar pressure. SOLUTION: A mixing amount of liquid-like fluororubber contains 10 to 100 pts.wt. with respect to 100 pts.wt. of polyol crosslinkable fluororubber. A mixing amount of polyol crosslinker is 0.1 to 10 pts.wt. A mixing amount of conductivity applicator is 5 to 1000 pts.wt. A mixing amount of stearic acid and its derivative is 0.1 to 10 pts.wt. Such a conductive fluororubber composition is molded by a planar pressure of 20 to 1000kg/cm<2> of pressing pressure. And a conductive fluororubber sheet having 20 or more of sheet area corresponding circular diameter/sheet thickness is manufactured. |