| 摘要 |
一种新型的透明玻璃陶瓷组合物，包括氧化物成分、稀土成分、卤化物成分和基本上纯的稀土卤化物(例如REF<SUB>3</SUB>)晶体成分。这种新材料的主要成分(摩尔百分含量)是SiO<SUB>2</SUB>(0—80);GeO<SUB>2</SUB>(0—80);Na<SUB>2</SUB>O(0—25);K<SUB>2</SUB>O(0—25);Rb<SUB>2</SUB>O(0—25);Cs<SUB>2</SUB>O(0—25);Al<SUB>2</SUB>O<SUB>3</SUB>(0—40);Ga<SUB>2</SUB>O<SUB>3</SUB>(0—40)RE<SUB>2</SUB>F<SUB>6</SUB>(0<RE<SUB>2</SUB>F<SUB>6</SUB><18);PbO(0—15)RO(0—25);ZnO(0—10);ZrO<SUB>2</SUB>(0—2);TiO<SUB>2</SUB>(0—2)Nb<SUB>2</SUB>O<SUB>5</SUB>(0—10);Ta<SUB>2</SUB>O<SUB>5</SUB>(0—10)P<SUB>2</SUB>O<SUB>5</SUB>(0—5);B<SUB>2</SUB>O<SUB>3</SUB>(0—15)As<SUB>2</SUB>O<SUB>3</SUB>(0—10);Sb<SUB>2</SUB>O<SUB>3</SUB>(0—10);和XCl<SUB>n</SUB>(0—5)，这里RO为BaO,CaO,SnO和MgO中的至少一种；XCl<SUB>n</SUB>是如NaCl、LaCl<SUB>3</SUB>、AlCl<SUB>3</SUB>或NH<SUB>4</SUB>Cl的含氯成分；而(SiO<SUB>2</SUB>+GeO<SUB>2</SUB>)为(40—80)；(Na<SUB>2</SUB>O+K<SUB>2</SUB>O+Rb<SUB>2</SUB>O+Cs<SUB>2</SUB>O)为(2—25)；(Al<SUB>2</SUB>O<SUB>3</SUB>+Ga<SUB>2</SUB>O<SUB>3</SUB>)为(10—40)，这里RE是Y<SUP>3+</SUP>,La<SUP>3+</SUP>,Ce<SUP>3+</SUP>,Pr<SUP>3+</SUP>,Nd<SUP>3+</SUP>,Sm<SUP>3+</SUP>,Eu<SUP>3+</SUP>,Gd<SUP>3+</SUP>,Tb<SUP>3+</SUP>,Dy<SUP>3+</SUP>,Ho<SUP>3+</SUP>,Er<SUP>3+</SUP>Tm<SUP>3+</SUP>,Yb<SUP>3+</SUP>和Lu<SUP>3+</SUP>中的一种或多种，单个或组合。在具体实施方案的一个方面，RE<SUB>2</SUB>F<SUB>6</SUB>的用量可根据以下公式选择：RE<SUB>2</SUB>F<SUB>6</SUB>＝(K)(R/r)<SUP> 3</SUP>(Al<SUB>2</SUB>O<SUB>3</SUB>+Ga<SUB>2</SUB>O<SUB>3</SUB>－R<SUB>2</SUB>O)2，这里R是Na、K、Rb和Cs其中之一；0.7≤K≤1.2；R是La<SUP>3+</SUP>的半径；r是RE<SUP>3+</SUP>的半径。一种制造此新材料的方法也被揭示，包括通过常规熔融方法制作一种含稀土离子的氟氧化物玻璃，使玻璃经受热处理(陶瓷化)，由此优选地沉析出含大量稀土离子的氟化物微晶。 |