WELDING MATERIAL FOR HEAT RESISTANT STEEL |
| 摘要 |
A welding material for heat resistant steel comprises: flux and a sheath surrounding the flux. The welding material comprises, by wt %, carbon (C): 0.03% to 0.3%, manganese (Mn): 0.5% to 3.0%, silicon (Si): 0.1% to 2.0%, phosphorus (P): 0.01% or less, sulfur (S): 0.01% or less, nickel (Ni): 20% to 40%, chromium (Cr): 15% to 35%, TiO2: 3% to 7%, SiO2: 0.5% to 2.5%, ZrO2: 0.5% to 2.5%, and a balance of Fe and inevitable impurities. The sheath comprises an Ni—Fe-based alloy having a nickel content of 30% to 50%. |
| 申请公布号 |
US2016318133(A1) |
申请公布日期 |
2016.11.03 |
| 申请号 |
US201315107633 |
申请日期 |
2013.12.24 |
| 申请人 |
POSCO |
发明人 |
HAN Il-Wook;KIM Jeong-Kil;LEE Bong-Keun;LEE Sang-Chul |
| 分类号 |
B23K35/36;C22C38/58;C22C38/50;C22C38/00;C22C38/42;C22C38/06;C22C38/04;C22C38/02;B23K35/30;C22C38/44 |
主分类号 |
B23K35/36 |
| 代理机构 |
|
代理人 |
|
| 主权项 |
1. A welding material for heat resistant steel, the welding material comprising flux and a sheath surrounding the flux,
wherein the welding material comprises, by wt %, carbon (C): 0.03% to 0.3%, manganese (Mn): 0.5% to 3.0%, silicon (Si): 0.1% to 2.0%, phosphorus (P): 0.01% or less, sulfur (S): 0.01% or less, nickel (Ni): 20% to 40%, chromium (Cr): 15% to 35%, TiO2: 3% to 7%, SiO2: 0.5% to 2.5%, ZrO2: 0.5% to 2.5%, and a balance of Fe and inevitable impurities, wherein the sheath comprises an Ni—Fe-based alloy having a nickel content of 30% to 50%. |