A process for manufacturing a dry-to-touch coating having corrosion resistance and torque is provided. The process comprises the steps of adding PTFE to an oil, with the oil containing a amine soap, thoroughly mixing the PTFE into the oil, forming a homogenous dispersion of the PTFE in the oil, mixing a resin forming paint component, adding water to the mixed paint component, mixing the resin forming paint component and water with the oil, and adjusting the pH. The resin forming paint component comprises in the range of 40% to 70% of the coating, the water comprises in the range of 5% to 10% of the coating, and the oil and PTFE blend comprises in the range of 10% to 30% of the coating. Additionally, the PTFE when added to the oil preferably comprises in the range of 10% to 30% by weight. The process further involves the exposure of the resin, water, and oil mixture to a temperature of between 175 DEG to 250 DEG F. until it is dry-to-touch.
|