| 摘要 |
<p>A film for stretch packaging comprising as a substrate a film of a linear low density polyethylene having a melt flow rate (190 DEG C), as measured by an ASTM-D-1238E method, of 0.3 to 8 g/10 min., a density, as measured by an ASTM-D-1505 method, of 0.900 to 0.918 g/cm<3>, a molecular weight distribution (Mw/Mn) of 2 to 6, two or more melting points existing as measured by a differential scanning calorimeter, a maximum melting point Tm1 of 118 to 125 DEG C and a ratio of the height Tm1H of the peak of the highest melting point Tm1 to the height Tm2H of the melting point Tm2 adjacent thereto (i.e., Tm1H/Tm2H), of 1.3 or less.</p> |