Method for making impact-absorptive material

摘要

A method for making an impact-absorptive material is introduced. The method involves mixing silicon dioxide (SiO2) particles, polydimethylsiloxane (PDMS), and an appropriate amount of an additive, allowing the mixture to settle until tiny bubbles in the mixture are evenly distributed, thereby forming a colloidal solution raw material, adding a crosslinking agent to the colloidal solution raw material to form a colloidal solution plastic material, filling a die with the colloidal solution plastic material, heating the colloidal solution plastic material in the die such that it takes shape and forms an effective impact absorbing material, quickly and at low costs, for use in physical education, medicine, transportation, and safety-enhancing equipment.

主权项

1. A method for making an impact-absorptive material, the method comprising the steps of:
(step 1) mixing silicon dioxide particles, polydimethylsiloxane (PDMS), and an additive, performing a compounding process on the mixture to form a liquid mixture essentially comprising silicon dioxide and PDMS, settling the liquid mixture until tiny bubbles therein are evenly distributed, and performing a ripening process on the liquid mixture to form a colloidal solution raw material; (step 2) adding a crosslinking agent to the colloidal solution raw material, mixing the crosslinking agent and the colloidal solution raw material until foaming occurs, so as to form a colloidal solution plastic material; and (step 3) filling a die with the colloidal solution plastic material, and heating the colloidal solution plastic material in the die to 80˜120° C. for 2˜4 hours until the colloidal solution plastic material cures to thereby allow the colloidal solution plastic material to take shape and form the impact-absorptive material; wherein the PDMS is of a molecular weight of 200˜5,000.