Manufacturing method for electric furnace steel for carburizing without Mo addition

摘要

An electric furnace steel contains, by mass %, C: 0.12 to 0.28%, Si: equal to or less than 0.15%, Mn: 0.65 to 0.95%, P: equal to or less than 0.035%, S: equal to or less than 0.035%, Cr: 1.35 to 1.90%, Al: 0.020 to 0.050%, and N: 0.0080 to 0.0230%. A scrap material is selected such that Cu, Ni, and Mo that derive from the scrap material and are thus contained as impurities in the electric furnace steel satisfy Expression 1. The electric furnace steel further contains Fe and unavoidable impurities as a remainder thereof. Accordingly, the electric furnace steel can secure carburizing quality equivalent to or higher than that of Cr—Mo steel, and can have properties equivalent to or higher than that of Cr—Mo steel, without adding Mo.
([Cu]+2×[Ni])0.76×[Mo]≧0.0040  Expression 1:

主权项

1. A manufacturing method for an electric furnace steel for carburizing, comprising the following components, in mass %:
C: 0.12 to 0.28%, Si: equal to or less than 0.15%, Mn: 0.65 to 0.95%, P: equal to or less than 0.035%, S: equal to or less than 0.035%, Cr: 1.35 to 1.90%, Al: 0.020 to 0.050%, and N: 0.0080 to 0.0230%, the electric furnace steel further comprising iron, wherein the method is performed without Mo addition by employing an electric furnace with a scrap material as a main raw material thereof, the method comprising: selecting the scrap material such that Cu, Ni, and Mo that are derived from the scrap material and are contained as impurities in the electric furnace steel satisfy Expression 1,
([Cu]+2×[Ni])0.76×[Mo]≧0.0040  Expression 1: where [Cu], [Ni], and [Mo] respectively mean contents (mass %) of Cu, Ni, and Mo in the steel and wherein the selecting does not comprise controlling a content of B; melting the scrap material by the electric furnace; and adding adjusting alloys for components excluding Cu, Ni and Mo of the electric furnace steel without intentionally adding Cu, Ni, and Mo; wherein Cu, Ni, and Mo that are contained as the impurities in the electric furnace steel satisfy Expression 1; and the contents of Cu, Ni and Mo are restricted to Cu: equal to or less than 0.30%, Ni: equal to or less than 0.25% and Mo: equal to or less than 0.06%.