Method for preparing lithium iron phosphate nanopowder |
摘要 |
The present invention relates to a method for preparing a lithium iron phosphate nanopowder, including the steps of (a) preparing a mixture solution by adding a lithium precursor, an iron precursor and a phosphorus precursor in a triethanolamine solvent, and (b) putting the mixture solution into a reactor and heating to prepare the lithium iron phosphate nanopowder under pressure conditions of 1 bar to 10 bar, and a lithium iron phosphate nanopowder prepared by the method. When compared to a common hydrothermal synthesis method, a supercritical hydrothermal synthesis method and a glycothermal synthesis method, a reaction may be performed under a relatively lower pressure. Thus, a high temperature/high pressure reactor is not necessary and process safety and economic feasibility may be secured. In addition, a lithium iron phosphate nanopowder having uniform particle size and effectively controlled particle size distribution may be easily prepared. |
申请公布号 |
US9543582(B2) |
申请公布日期 |
2017.01.10 |
申请号 |
US201414510356 |
申请日期 |
2014.10.09 |
申请人 |
LG Chem, Ltd. |
发明人 |
Jun In Kook;Cho Seung Beom;Oh Myoung Hwan |
分类号 |
C01B25/45;H01M4/58;H01M4/36;H01M4/04;H01M4/136;H01M4/587;H01M10/052;H01M4/02;H01M4/62 |
主分类号 |
C01B25/45 |
代理机构 |
Lerner, David, Littenberg, Krumholz & Mentlik, LLP |
代理人 |
Lerner, David, Littenberg, Krumholz & Mentlik, LLP |
主权项 |
1. A method for preparing a lithium iron phosphate nanopowder, comprising the steps of:
(a) preparing a mixture solution by adding a lithium precursor, an iron precursor and a phosphorus precursor in a triethanolamine solvent, which is a non-aqueous solvent; and (b) putting the mixture solution into a reactor and heating to prepare the lithium iron phosphate nanopowder under pressure conditions of 1 bar to 10 bar and at a temperature range of 150 to 335° C. |