发明名称 |
Process for manufacturing a tin-plated sheet with higher corrosion resistance |
摘要 |
<p>Steel sheet containing 10-500 ppm of carbon is cold rolled. The oil used, has a viscosity in the range 30-70 mm<2>/s measured at 50 degrees C. The steel sheet is annealed, causing recrystallization. The surface to be coated is pickled in a mineral acid, and is then coated in a tin bath of high purity. In this way, between the tin layer and the steel sheet, a tin/steel boundary layer (diffusion layer) is formed. An Independent claim is included for corresponding tinplate.</p> |
申请公布号 |
EP1106707(B1) |
申请公布日期 |
2009.07.22 |
申请号 |
EP20000126368 |
申请日期 |
2000.12.02 |
申请人 |
RASSELSTEIN GMBH |
发明人 |
BECKER, ROLF;THRAN, DIETMAR;OBERHOFFER, DR. HELMUT;SAUER, DR. REINER |
分类号 |
C23C2/08;C25D3/30;G01N17/02 |
主分类号 |
C23C2/08 |
代理机构 |
|
代理人 |
|