Silicone rubber composition for coating for woven fabric, and coated woven fabric

摘要

A silicone-rubber composition for coating textile fabrics characterized in that the silicone-rubber composition comprises the following components: an alkenyl group-containing organopolysiloxane (A) that comprises a mixture of an organopolysiloxane (A-1) that contains in one molecule at least two alkenyl groups in the amount not exceeding 2 mass % and an organopolysiloxane (A-2) that contains in one molecule at least two alkenyl groups in amount of 5 mass % or more; an organohydrogenpolysiloxane (B) that comprises a mixture of an organohydrogenpolysiloxane (B-1) that has in one molecule on average three silicon-bonded hydrogen atoms and an organohydrogenpolysiloxane (B-2) that has in one molecule on average two silicon-bonded hydrogen atoms; a hydrosilylation catalyst (C); and a reinforcement fine silica powder (D); and elongation according to JIS K6251 of the cured product of the composition is equal to or greater than 800%.

主权项

1. A silicone-rubber composition for coating textile fabrics characterized in that the silicone-rubber composition comprises the following components:
100 parts by mass of an alkenyl group-containing organopolysiloxane (A) that comprises a mixture of an organopolysiloxane (A-1) having in one molecule at least two alkenyl groups in an amount not exceeding 2 mass % and an organopolysiloxane (A-2) that contains in one molecule at least two alkenyl groups in an amount of 5 mass % or more, wherein the constituent (A-2) is contained in the amount of 1 part by mass or less than 1 part by mass for 100 parts by mass of constituent (A-1), and wherein the mole number of alkenyl groups contained in constituent (A-2) is 0.5 to 2 times the mole number of alkenyl groups contained in constituent (A-1); an organohydrogenpolysiloxane (B) that comprises a mixture of an organohydrogenpolysiloxane (B-1) that has on average three silicon-bonded hydrogen atoms in one molecule and an organohydrogenpolysiloxane (B-2) that has on average two silicon-bonded hydrogen atoms in one molecule, wherein the constituents (B-1) and (B-2) are mixed in such a ratio that the mole ratio of silicon-bonded hydrogen atoms of constituent (B-1) to silicon-bonded hydrogen atoms of constituent (B-2) is in the range of (1.0:0) to (1.0:1.0), and wherein the mole ratio of silicon-bonded hydrogen atoms of constituent (B) to alkenyl groups of constituent (A) ranges from (0.9:1.0) to (2.5:1.0); a hydrosilylation catalyst (C) in an amount required for curing the composition; 0.1 to 50 parts by mass of a reinforcement fine silica powder (D); and an adhesion promoter selected from the group consisting of: a combination of a methacryloxy-containing organoalkoxysilane compound and a zirconium-chelate compound; and a combination of a methacryloxy-containing organoalkoxysilane compound, an epoxy-containing organoalkoxysilane compound, and a zirconium-chelate compound, wherein the adhesion promoter is present in an amount of 0.05 to 5 parts by mass per 100 parts by mass of component (A); wherein elongation according to JIS K6251 of the cured product of the composition is equal to or greater than 800%; and wherein the silicone-rubber composition has a viscosity at 25° C. in the range of 100 to 500 Pa·s.