Ceramic for ignition device insulator with low relative permittivity

摘要

A ceramic insulator for surrounding an electrode of an ignition device, such as a corona igniter or spark plug, is provided. The insulator is formed of a ceramic material including alumina in an amount of 28 to 38 wt. %, silica in an amount of 57 to 67 wt. %, and calcium oxide in an amount of 3 to 7 wt. %, based on the total weight of the ceramic material. The ceramic insulator is typically formed by firing a mixture of Kaolin, calcium carbonate, and silica, wherein the calcium carbonate acts as a flux during firing. The ceramic material has a relative permittivity of about 5.5 to 6.5 and thus improves the electrical efficiency of the ignition device. The ceramic material is also capable of withstanding temperatures of 900 to 1000° C. and has excellent thermal shock resistance, making it suitable for use in internal combustion engines.

主权项

1. An insulator for an ignition device, comprising:
a ceramic material including alumina in an amount of 28 to 38 wt. %, silica in an amount of 57 to 67 wt. %, and calcium oxide in an amount of 3 to 7 wt. %, based on the total weight of said ceramic material.