HIGH STRENGTH AND HIGH FORMABILITY STEEL SHEET AND MANUFACTURING METHOD THEREOF |
摘要 |
A high strength and high formability steel sheet contains, by mass % of the steel sheet: greater than 0.020% and less than 0.040% of C; not less than 0.003% and not greater than 0.100% of Si; not less than 0.10% and not greater than 0.60% of Mn; not less than 0.001% and not greater than 0.100% of P; not less than 0.001% and not greater than 0.020% of S; not less than 0.005% and not greater than 0.100% of Al; and greater than 0.0130% and not greater than 0.0170% of N, wherein a remainder is Fe and inevitable impurities, and the steel sheet has: a tensile strength in a rolling direction of not lower than 520 MPa; an Erichsen value of not less than 5.0 mm; and a resin film layer at least on a side to be an inner surface of a can. |
申请公布号 |
US2015064448(A1) |
申请公布日期 |
2015.03.05 |
申请号 |
US201314382363 |
申请日期 |
2013.04.03 |
申请人 |
JFE Steel Corporation |
发明人 |
Tanaka Takumi;Kojima Katsumi;Tobiyama Yoichi |
分类号 |
C25D5/36;C21D1/26;C21D8/02 |
主分类号 |
C25D5/36 |
代理机构 |
|
代理人 |
|
主权项 |
1. A high strength and high formability steel sheet comprising:
a steel sheet layer comprising, in mass %, greater than 0.020% and less than 0.040% of C; not less than 0.003% and not greater than 0.100% of Si; not less than 0.10% and not greater than 0.60% of Mn; not less than 0.001% and not greater than 0.100% of P; not less than 0.001% and not greater than 0.020% of S; not less than 0.005% and not greater than 0.100% of Al; greater than 0.0130% and not greater than 0.0170% of N; a remainder being Fe and inevitable impurities; and a resin film layer on at least one side of the steel sheet layer; the steel sheet having: a tensile strength in a rolling direction of not less than 520 MPa; and an Erichsen value of not less than 5.0 mm. |