| 摘要 |
<p>A high strength pressed member having excellent ductility and stretch flangeability and tensile strength of 780-1400 MPa, with predetermined steel composition and steel microstructure relative to the entire microstructure of steel sheet, where area ratio of martensite 5-70%, area ratio of retained austenite 5-40%, area ratio of bainitic ferrite in upper bainite 5% or more, and total thereof is 40% or more, 25% or more of martensite is tempered martensite, polygonal ferrite area ratio is above 10% and below 50% to the entire microstructure of steel sheet, and average grain size is 8 µm or less, average diameter of a group of polygonal ferrite grains is 15 µm or less, the group of polygonal ferrite grains represented by a group of ferrite grains of adjacent polygonal ferrite grains, and average carbon content in retained austenite is 0.70 mass % or more and tensile strength is 780 MPa or more.</p> |