STRAIN AGING HARDENING TYPE STEEL SHEET EXCELLENT IN AGING RESISTANCE, AND MANUFACTURING METHOD THEREOF

摘要

A strain aging hardening type steel sheet excellent in aging resistance, and manufacturing method thereof, said steel sheet comprises: in mass %, C: 0.0010 to 0.010%; Si: 0.005 to 1.0%; Mn: 0.08 to 1.0%; P: 0.003 to 0.10%; S: 0.0005 to 0.020%; Al: 0.010 to 0.10%; Cr: 0.005 to 0.20%; Mo: 0.005 to 0.20%; Ti: 0.002 to 0.10%; Nb: 0.002 to 0.10%; N: 0.001 to 0.005%; and a balance being composed of Fe and inevitable impurities, in which a ferrite fraction is 98% or more, an average grain diameter of ferrite is 5 to 30 mum, a minimum value of dislocation density in a portion having a ½ thickness of a sheet thickness and a minimum value of dislocation density in a surface layer portion are each 5×1012/m2 or more, and an average dislocation density falls within a range of 5×1012 to 1×1015/m2.