| 摘要 |
A multistage method for treatment of composite metal structures containing metallic surfaces of aluminum, zinc and optionally iron, is provide wherein in a first step, selective zinc phosphating of zinc and ferrous surfaces proceeds using a phosphating solution containing a quantity of water-soluble inorganic silicon compounds sufficient to suppress white spot formation on zinc, but less than the quantity where zinc phosphating loses selectivity. In a following second step, aluminum surfaces are passivated with an acidic treatment solution. Also provided is a zinc phosphating solution suitable for said method containing at least 0.025 g/l, but less than 1 g/l of silicon as water-soluble inorganic compounds calculated as SiF6, wherein the product (Si/mM)·(F/mM) of the concentration of silicon [Si in mM] in the form of water-soluble inorganic compounds and the concentration of free fluoride [F in mM] divided by the free acid point number is no greater than 5.
|