Disclosed are a high-strength, high-toughness hot-pressed steel plate member and a manufacturing method therefor. A specified hot-press process is performed on a steel plate member that, with respect to the chemical composition of the steel plate, includes: 0.15 to 0.4 wt % of C; 1.0 to 5.0 wt % of Mn or of a total of Mn and at least one of Cr, Mo, Cu, and Ni; 0.02 to 2.0 wt % of at least any one of Si and Al; and the remainder being Fe and unavoidable impurities, thus providing the physical properties of a martensite phase average grain diameter of 5 mum or less and a tensile strength of 1200 MPa or higher.
|