| 摘要 |
Disclosed is a MnZnCo-based ferrite consisting of base constituents, accessory constituents, and inevitable impurities, which MnZnCo-based ferrite is characterized by adding silicon oxide (SiO2 conversion): 50-400 mass ppm and calcium oxide (CaO conversion): 1000-4000 mass ppm as secondary constituents to base constituents consisting of iron oxide (Fe2O3 conversion): 51.0-53.0 mol %, zinc oxide (ZnO conversion): greater than 12.0 mol % and less than 18.0 mol %, cobalt oxide (CoO conversion): 0.04-0.60 mol %, and manganese oxide (MnO conversion): remainder, and keeping phosphorus, boron, sulfur, and chlorine of the inevitable impurities to phosphorous: less than 3 mass ppm, boron: less than 3 mass ppm, sulfur: less than 5 mass ppm, and chlorine: less than 10 mass ppm. This MnZnCo-based ferrite has the superior characteristics of always having incremental permeability [mu]? of 2000 or greater across a wide temperature range of−40 DEG C. to 85 DEG C. when a 33 A/m direct current magnetic field is applied, even in cases when formed into a small core with outside diameter of approximately 2-6 mm.
|