发明名称 |
FIBER-REINFORCED COMPOSITE MATERIAL, METHOD FOR PRODUCING THE SAME, AND WIRING BOARD |
摘要 |
PROBLEM TO BE SOLVED: To provide a fiber-reinforced composite material in which high transparency is always maintained without being affected by temperature conditions, wavelengths, and the like, and various types of functionality are imparted by forming a composite between fibers and a matrix material.SOLUTION: There is provided a fiber-reinforced composite material containing fibers having an average fiber diameter of 4 to 200 nm and a matrix material, and having a visible light transmittance of 60% or more at a wavelength of 400 to 700 nm, which is a conversion value based on a thickness of 50 μm. Since fibers having an average fiber diameter of shorter than the wavelength of visible light (380-800 nm) are used, the refraction of visible light by the fibers is hard to occur, and even if a temperature change and a wavelength variation occur, the scattering loss of visible light at the interface of fibers and the matrix material is hard to be generated. Therefore, a high transparency of a visible light transmittance of 60% or more in terms of 50 μm thickness can be held with stability. |
申请公布号 |
JP2011001559(A) |
申请公布日期 |
2011.01.06 |
申请号 |
JP20100210626 |
申请日期 |
2010.09.21 |
申请人 |
KYOTO UNIV;ROHM CO LTD;MITSUBISHI CHEMICALS CORP;HITACHI LTD;PIONEER ELECTRONIC CORP;NIPPON TELEGR & TELEPH CORP <NTT> |
发明人 |
YANO HIROYUKI;SUGIYAMA JUNJI;ATAGI MASAYA;IWAMOTO SHINICHIRO;KURIHARA TAKASHI;MATSUURA TORU;HANDA KEISHIN;NAGAI AKIRA;MIWA TAKAO;TAKEZAWA YOSHITAKA |
分类号 |
C08J5/04;C08J5/00;C08K7/02;C08L101/00;G02B6/10;G02B6/12;G02B6/122;G02B6/42;H05K1/03 |
主分类号 |
C08J5/04 |
代理机构 |
|
代理人 |
|
主权项 |
|
地址 |
|