ТЕРМОСТОЙКИЕ ЛЕГИРОВАННЫЕ И НЕЛЕГИРОВАННЫЕ ПОРИСТЫЕ ОКСИДЫ АЛЮМИНИЯ И НАНОКОМПОЗИТЫ, СОДЕРЖАЩИЕ СМЕСЬ ОКСИДОВ CeO2-ZrO2 И Al2O3

摘要

The present invention relates to doped or undoped aluminas having after calcination at 1200° C. for 5-24 hours a pore volume >=0.5 ml/g and a BET surface area greater then 35 m2/g. The invention also relates to a method for preparing these aluminas comprising the steps of: a. preparing an aqueous solution of an aluminum salt with optional co-dopants, b. treating the aqueous solution with hydrogen peroxide, c. precipitating the alumina using a base, and d. filtering, drying and calcining the alumina.