Separator für Brennstoffzellenbatterie und Verfahren zu dessen Herstellung

摘要

In a separator for a fuel cell and a method of producing a separator for a fuel cell according to the invention, bond-carbon is used in which composition ratios are set to 60 to 90 wt.% (preferably, 70 to 87 wt.%) of graphite powder having an average diameter in a range of 15 to 125 µm (preferably, 40 to 100 µm), and 10 to 40 wt.% (preferably, 13 to 30 wt.%) of a thermosetting resin. The compound is previously cold-molded into a shape similar to a final molded shape. The preliminary molded member is then placed in a mold, and then molded into a separator of the final shape by applying a pressure of a range of 10 to 100 MPa. The surface roughness Ra of at least a portion of the separator contacting with an electrode is set to a range of 0.1 to 0.5 µm. According to this configuration, fluidity and moldability are excellent, the contact resistance can be set to a value lower than a requested value while ensuring strength sufficient for preventing the separator from suffering a damage such as a breakage due to vibrations or the like, and the low contact resistance can be stably maintained.