<p>This invention relates to a mixture comprising the following proportion of masses: from 0.4 to 4 %, preferably 0.8 to 1.7 %, content of ultrafine grain size materials constituted by D90 particles measuring less than 1 mum and/or a BET specific surface area greater than 6 m2/g; from 1 to 6 %, preferably 2 to 5 %, of Portland cement; from 8 to 25 %, preferably 12 to 21 %, of fine grain size materials constituted by particles whose DlO and D90 are between 1 mum and 100 mum and have a BET specific surface less than 5 m2/g, both different from the cement; from 25 to 50 %, preferably 30 to 42 %, of medium grain size materials constituted by particles whose Dl 0 and D90 are between 100 mum and 5 mm and from 25 to 55 %, preferably 35 to 47 %, of superior grain size material constituted by particles whose Dl 0 which is greater than 5 mm. The invention also concerns, in particular, premixed concrete compositions and combined hardened concrete, as well as their preparation processes.</p> |