Glass and optical glass element

摘要

Disclosed herein is a glass whose viscosity index (A) defined as a value obtained by dividing the viscosity of the glass at the liquidus temperature thereof by the liquidus temperature of the glass is in the range of 0.0004 to 1.5. Such a glass is melted in a melting furnace equipped with a nozzle, and the molten glass is dropped from the nozzle intermittently and regularly to obtain glass droplets. The glass droplet naturally dropped from the nozzle is received by a receiving mold to form a glass gob. The glass gob can be used as a preform for reheating molding. Further, it is possible to produce an optical glass element having no plane defect such as a shear mark by press-molding a hot glass gob with an upper mold just after the glass gob is received by the receiving mold.