A niobium powder for a capacitor having a tapping density of 0.5 to 2.5 g/ml, and average particle size of 10 to 1000 mumum, angle of repose form 10° to 60°, the BET specific surface area from 0.5 to 40 m<SUP>2</SUP>/g and a plurity of pore diameter peak tops in the pore distribution, and a producing method therof; (2) a niobium sintered body, which is obtained by sintering the above niobium powder and, having a plurality of pore diameter peak tops in a range of 0.01 mumum to 500 mumum, preferably, the peak tops of two peaks among the plurality of pore diameter peak tops having a highest relative intensity are present in the range of 0.2 to 0.7 mumum and in the range of 0.7 to 3 mumum, respectively, and a producing method thereof; (3) a capacitor using the above sintered body and a producing method thereof, and (4) an electronic circuit and electronic device using the above capacitor. |