Golf club head used in golf club manufacture is made from a rust-free age-hardened maraging steel containing alloying additions of nickel, chromium, titanium, beryllium |
摘要 |
Golf club head is made from a rust-free age-hardened maraging steel having a martensitic temperature MS of at least 130 degrees C and a ferrite content of less than 3 %. The maraging steel contains (in weight %) 6.0-9.0 nickel, 11.0-15.0 chromium, 0.1-0.3 titanium, 0.2-0.3 beryllium, and a balance of iron. The steel has a tensile strength of more than 2000 MPa and a creep limit of more than 1900 MPa. An Independent claim is also included for a process for the production of a maraging steel for a golf club head comprising melting a maraging steel alloy and casting to form a cast block, hot deforming the block to form a green body, solution annealing, cooling, grinding to remove beryllium-deficient edge zones, cold deforming, and heat treating. |
申请公布号 |
DE10242322(A1) |
申请公布日期 |
2004.04.01 |
申请号 |
DE2002142322 |
申请日期 |
2002.09.12 |
申请人 |
VACUUMSCHMELZE GMBH & CO. KG |
发明人 |
WEBER, HARTWIN;DOERING, WALDEMAR;FACKELMANN, DOMINIK |
分类号 |
A63B53/04;C21D6/00;C21D6/02;C21D8/00;C21D9/00;C22C38/00;C22C38/44;C22C38/50;(IPC1-7):C22C38/50 |
主分类号 |
A63B53/04 |
代理机构 |
|
代理人 |
|
主权项 |
|
地址 |
|