Pyrolytic boron nitride crucible and method

摘要

A method of forming a pyrolytic boron nitride (PBN) article and an article having layers of PBN separated by layers of PBN having a dopant of sufficient concentration to induce peeling, the steps of introducing vapors of ammonia and a gaseous boron halide in a suitable ratio into a heated furnace reactor to cause boron nitride to be deposited in layers on a substrate, with at least one gaseous dopant injected into furnace at controlled periodic interval(s) such that at least two selected layers of boron nitride are doped with said gaseous dopant(s) at a minimum average concentration of 2 atomic wt % at a depth ranging from 1000 to 2000 angstroms in each selected layer, and with the selected layers spaced apart about 0.1 micron to 100 microns apart.