The invention relates to a high strength hot-dip galvanized steel sheet consisting essentially of 0.03 to 0.25% C, 0.7% or less Si, 1.4 to 3.5% Mn, 0.05% or less P, 0.01% or less S, 0.05 to 1% Cr, 0.005 to 0.1% Nb, by mass, and balance of Fe, and being made of a composite structure of ferrite and secondary phase, and having an average grain size of the composite structure of 10 mu m or smaller. Since the high strength hot-dip galvanized steel sheet of the present invention hardly induces softening at HAZ during welding, it is applicable to structural members of automobiles for "Tailor Welded Blanks" (TWB). <IMAGE> |